SLA Material – Flame Retardant Resin

Flame Retardant Resin For Excellent Part Quality And Heat Resistance.

Easily and quickly create stiff, creep-resistant, and functional plastic parts that perform well long-term in indoor and industrial environments. FR Resin is self-extinguishing and halogen-free with favorable flame, smoke, and toxicity (FST) ratings.

Common Applications:

Custom jigs, fixtures, and replacement parts for industrial environments with high temperatures or ignition sources.
Protective and internal consumer or medical electronics components.
Low quantity production of small parts.
Interior parts in airplanes, automobiles, and railways with excellent surface finish.

SLA: Flame Retardant Technical Specifications:


MATERIAL PROPERTIES DATA
	Metric	ENGLISH	METHOD
Tensile Properties
Ultimate Tensile Strength	38 MPa	5590 psi	ASTM D638-14
Tensile Modulus	2.9 GPa	430 ksi	ASTM D638-14
Elongation at Break	9.4%	9.40%	ASTM D638-14
Flexural Properties
Flexural Modulus	2.7 GPa	392 ksi	ASTM D790-15
Impact Properties
Notched Izod	22 J/m	0.41 ft-lbs/in	ASTM D256-10
Thermal Properties
Heat Deflection Temp. @ 1.8 MPa	71 °C	160 °F	ASTM D648-16
Heat Deflection Temp. @ 0.45 MPa	94 °C	201 °F	ASTM D648-16
Coefficient of Thermal Expansion, 20°- 80°C	98.6 μm/m/°C	54.8 μin/in/°F	ASTM E813-13

SLA: Flame Retardant Solvent Compatibility:


SOLVENT COMPATIBILITY DATA
Percent weight gain over 24 hours for a printed and post-cured 1 x 1 x 1 cm cube immersed in respective solvent
Solvent
Hydrochloric Acid (10%)	< 0.1
Acetone	2.1
Bleach ~5% NaOCl	0.3
Butyl Acetate	0.4
Diesel Fuel	< 0.1
Diethyl glycol Monomethyl Ether	0.3
Hydraulic Oil	< 0.1
Hydrogen peroxide (3%)	1
Isooctane (aka gasoline	< 0.1
Isopropyl Alcohol	0.2
Mineral oil (Light)	< 0.1
Mineral oil (Heavy)	< 0.1
Salt Water (3.5% NaCl)	0.2
Skydrol 5	< 0.1
Sodium Hydroxide solution (0.025% PH 10)	0.3
Power Steering Fluid	< 0.1
Brake Fluid (Castrol DOT-4)	< 0.1
Engine Oil (Havoline SAE 5W-30	< 0.1