High Temp Resin offers a heat deflection temperature (HDT) of 238 °C @ 0.45 MPa, the highest among Formlabs resins. Use it to print detailed, precise prototypes with high temperature resistance.
For data on post cure + additional thermal cure see full spec sheet.
MATERIAL PROPERTIES DATA | |||
Metric | ENGLISH | METHOD | |
Tensile Properties | |||
Ultimate Tensile Strength | 58 MPa | 8456 psi | ASTM D638-14 |
Tensile Modulus | 2.8 GPa | 399 ksi | ASTM D638-14 |
Elongation at Break | 3.3% | 3.3% | ASTM D638-14 |
Flexural Properties | |||
Flexural Modulus | 2.6 GPa | 400 ksi | ASTM D 790-15 |
Impact Properties | |||
Notched Izod | 18 J/m | 0.34 ft-lbf/in | ASTM D256-10 |
Thermal Properties | |||
Heat Deflection Temp. @ 1.8 MPa | 78 °C | 172 °F | ASTM D 648-16 |
Heat Deflection Temp. @ 0.45 MPa | 120 °C | 248 °F | ASTM D 648-16 |
Thermal Expansion | 80 μm/m/°C | 44 μin/in/°F | ASTM E 831-13 |
SOLVENT COMPATIBILITY DATA | |
Percent weight gain over 24 hours for a printed and post-cured 1 x 1 x 1 cm cube immersed in respective solvent | |
Solvent | 24 hr weight gain, % |
Acetic Acid 5% | < 1 |
Acetone | 2 |
Bleach ~5% NaOCl | < 1 |
Butyl Acetate | < 1 |
Diesel Fuel | < 1 |
Diethyl glycol Monomethyl Ether | 1 |
Hydraulic Oil | < 1 |
Hydrogen peroxide (3%) | < 1 |
Isooctane (aka gasoline | < 1 |
Isopropyl Alcohol | < 1 |
Mineral oil (Light) | < 1 |
Mineral oil (Heavy) | < 1 |
Salt Water (3.5% NaCl) | < 1 |
Skydrol 5 | 1.1 |
Sodium Hydroxide solution (0.025% PH 10) | < 1 |
Strong Acid (HCl conc) | < 1 |
Water | < 1 |
Xylene | < 1 |
DOWNLOAD THE FULL MATERIAL DATA SHEET