SLA Material – Tough 2000 Resin

Tough 2000 Resin for Rugged Prototyping

Tough 2000 Resin is the strongest and stiffest material in our functional family of Tough and Durable Resins. Choose Tough 2000 Resin for prototyping strong and sturdy parts that should not bend easily. Strong and stiff prototypes. Sturdy jigs and fixtures. ABS-like strength and stiffness.

Common Applications:

Ridged prototypes
Tough fixtures
Low quantity production
Wear resistant parts
Medical models and devices
Medical Models and Medical Devices

SLA: Tough 2000 Technical Specifications:


MATERIAL PROPERTIES DATA
	Metric	ENGLISH	METHOD
Tensile Properties
Ultimate Tensile Strength	46 MPa	6671 psi	ASTM D 638-14
Tensile Modulus	2.2 GPa	329 ksi	ASTM D 638-14
Elongation at Break	48 %	48 %	ASTM D 638-14
Flexural Properties
Flexural Modulus	1.9 GPa	275 ksi	ASTM D 790-15
Impact Properties
Notched Izod	40 J/m	0.75 ft-lbf/in	ASTM D256-10
Thermal Properties
Heat Deflection Temp. @ 1.8 MPa	53 °C	127 °F	ASTM D 648-16
Heat Deflection Temp. @ 0.45 MPa	63 °C	145 °F	ASTM D 648-16

SLA: Tough 2000 Solvent Compatibility:


SOLVENT COMPATIBILITY DATA
Percent weight gain over 24 hours for a printed and post-cured 1 x 1 x 1 cm cube immersed in respective solvent
Solvent	24 hr weight gain, %
Acetic Acid 5%	0.71
Acetone	18.82
Bleach ~5% NaOCl	0.56
Butyl Acetate	6.19
Diesel Fuel	0.06
Diethyl glycol Monomethyl Ether	5.32
Hydraulic Oil	0.08
Hydrogen peroxide (3%)	0.63
Isooctane (aka gasoline	0.03
Isopropyl Alcohol	3.7
Mineral oil (Light)	0.13
Mineral oil (Heavy)	0.17
Salt Water (3.5% NaCl)	0.56
Skydrol 5	0.87
Sodium Hydroxide solution (0.025% PH 10)	0.61
Strong Acid (HCl conc)	3.01
Water	0.61
Xylene	4.1